JDR Woodhead Publishing
HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
QUICK SEARCH:   [advanced]


     

This Article
Right arrow Full Text (PDF)
Services
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Download to citation manager
Citing Articles
Right arrow Citing Articles via Google Scholar
Google Scholar
Right arrow Articles by Watanabe, I.
Right arrow Articles by Okabe, T.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Watanabe, I.
Right arrow Articles by Okabe, T.

Journal of Dental Research, Vol 76, 773-779, Copyright © 1997 by International & American Associations for Dental Research Online Journals

ARTICLES

Effect of pressure difference on the quality of titanium casting

I. Watanabe, J. H. Watkins, H. Nakajima, M. Atsuta and T. Okabe
Department of Biomaterials Science, Baylor College of Dentistry-Texas A&M University System, Dallas 75246, USA.

In casting titanium using a two-compartment casting machine, Hero et al. (1993) reported that the pressure difference between the melting chamber and the mold chamber affected the soundness of the castings. This study tested the hypothesis that differences in pressure produce castings with various amounts of porosity and different mechanical properties values. Plastic dumbbell-shaped patterns were invested with an alumina-based, phosphate-bonded investment material. Both chambers of the casting machine were evacuated to 6 x 10(-2) torr; the argon pressure difference was then adjusted to either 50, 150, 300, or 450 torr. The porosity of the cast specimens was determined by x-ray radiography and quantitative image analysis. Tensile strength and elongation were measured by means of a universal testing machine at a strain rate of 1.7 x 10(-4)/s. The fractured surfaces were examined by SEM. Changes in Vickers hardness with depth from the cast surface were measured on polished cross-sections of the specimens. Raising the argon pressure difference to 300 and 450 torr caused a significant increase in internal porosity and a resultant decrease in the engineering tensile strength and elongation. The highest tensile strength (approximately 540 MPa), elongation (approximately 10%), bulk hardness (HV50g 209), and lowest porosity level (approximately 0.8%) occurred in the specimens cast at 150 torr. Turbulence of the metal during casting was thought to be responsible for the increase in porosity levels with the increase in argon pressure difference. By choosing an argon pressure difference (around 150 torr) suitable for this geometry, we could produce castings which have adequate mechanical properties and low porosity levels.




HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
IADR Journals Advances in Dental Research ®
Journal of Dental Research ® Critical Reviews (1990-2004)
Copyright © 1997 Institutional Access Guidelines