JDR JDR Most Cited Articles
HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
QUICK SEARCH:   [advanced]


     

This Article
Right arrow Full Text (PDF)
Services
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Download to citation manager
Citing Articles
Right arrow Citing Articles via Google Scholar
Google Scholar
Right arrow Articles by Van Meerbeek, B.
Right arrow Articles by VanHerle, G.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Van Meerbeek, B.
Right arrow Articles by VanHerle, G.

Journal of Dental Research, Vol 72, 495-501, Copyright © 1993 by International & American Associations for Dental Research Online Journals

ARTICLES

Comparative SEM and TEM examination of the ultrastructure of the resin-dentin interdiffusion zone

B. Van Meerbeek, A. Dhem, M. Goret-Nicaise, M. Braem, P. Lambrechts and G. VanHerle
Department of Operative Dentistry and Dental Materials, Katholieke Universiteit, Leuven, Belgium.

The resin-dentin interdiffusion zone produced by a dentin-adhesive system that removes the smear layer and concurrently decalcifies superficial dentin was morphologically examined by both scanning and transmission electron microscopy. Cross-sectioned resin-bonded dentin discs were etched with an argon-ion beam to make the resin-dentin interface observable by SEM. For the TEM examination, the sections were partly decalcified by an aqueous EDTA solution to facilitate ultramicrotomy and to disclose the ultrastructure of the interdiffusion zone. Both SEM and TEM confirmed the presence of the resin-dentin interdiffusion zone as the junction between the deep unaltered dentin structure and the restorative resin. Within the interdiffusion zone, three sublayers with characteristic ultrastructure and staining were identified by TEM. An upper diffuse black layer contained few structural features. Underneath, partially-altered collagen fibrils were closely packed, mostly running parallel with the interface and perpendicular to the dentinal tubules. Their outline was electron-dense, forming tunnel-like structures. At the base of the upper layer, several stained projections were found to bulge out into the underlying collagen network and appeared to be confined by obstructive, parallel-running collagen fibrils. Finally, the third dense layer, containing hydroxyapatite crystals, demarcated the superficially demineralized dentin layer from the deeper unaltered dentin. Resin diffusion into the decalcified dentin surface layer was evident, but diminished with depth, presumably reducing deeper resin impregnation into the interfibrillar spaces. The citric acid dentin-pretreatment probably caused denaturation of the superficial collagen fibrils. Its decalcifying effect gradually weakened with depth, leaving behind hydroxyapatite crystals at the base of the interdiffusion zone.(ABSTRACT TRUNCATED AT 250 WORDS)




HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
IADR Journals Advances in Dental Research ®
Journal of Dental Research ® Critical Reviews (1990-2004)
Copyright © 1993 Institutional Access Guidelines