JDR Woodhead Publishing
HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
QUICK SEARCH:   [advanced]


     

This Article
Right arrow Full Text (PDF)
Services
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Download to citation manager
Citing Articles
Right arrow Citing Articles via Google Scholar
Google Scholar
Right arrow Articles by Zuellig-Singer, R.
Right arrow Articles by Lutz, F.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Zuellig-Singer, R.
Right arrow Articles by Lutz, F.

Journal of Dental Research, Vol 71, 1842-1846, Copyright © 1992 by International & American Associations for Dental Research Online Journals

ARTICLES

Effects of cement-curing modes on dentin bonding of inlays

R. Zuellig-Singer, I. Krejci and F. Lutz
Department of Preventive Dentistry, Periodontology and Cariology, University of Zurich, Switzerland.

The aim of this in vitro study was to evaluate dentin adhesion after cementation of immediate direct "All Purpose" Hybrid (AP.H) composite inlays (Dentsply) and Cerec Dicor-MGC (Dentsply) inlays with the dentin adhesive Prisma Universal Bond 2 (Dentsply) and the dual-curing Dicor-MGC luting composite (Dentsply). In 24 extracted human molars, standard MOD cavities were prepared with one approximal margin located in enamel and the other one located in dentin. They were divided into four groups: (I) AP.H inlays, luting composite only, chemically cured; (II) AP.H inlays, luting composite, immediately-light-cured; (III) AP.H inlays, luting composite, initially chemically and delayed-light-cured (15 min); and (IV) MGC inlays, luting composite, initially chemically and delayed-light-cured (15 min). In vitro load cycles corresponding to five years of clinical stress followed. Initially and after specimens were loaded, the margins were analyzed quantitatively by SEM. The tooth/cement and cement/inlay interfaces were scored separately. The initial percentages of "continuous margin"--at both the tooth/luting composite and luting composite/inlay interfaces--were higher than 94% for all groups. At the end of the load cycles, the quality of the margins at the tooth/luting composite interface significantly decreased for all groups. The highest decrease was found for the cervical margins located in dentin, where only 37%-61% were scored as "continuous margin". The AP.H inlay/luting composite interface showed almost no change. At the MGC inlay/luting composite interface, the percentage of "continuous margin" decreased to 74%. After specimens were loaded, the percentage of "continuous margin" in dentin was lower than in enamel, despite the use of a dentin bonding agent (PUB 2).(ABSTRACT TRUNCATED AT 250 WORDS)




HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
IADR Journals Advances in Dental Research ®
Journal of Dental Research ® Critical Reviews (1990-2004)
Copyright © 1992 Institutional Access Guidelines