JDR Woodhead Publishing
HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
QUICK SEARCH:   [advanced]


     

This Article
Right arrow Full Text (PDF)
Services
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Download to citation manager
Citing Articles
Right arrow Citing Articles via Google Scholar
Google Scholar
Right arrow Articles by Jones, D. W.
Right arrow Articles by Robertson, K. N.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Jones, D. W.
Right arrow Articles by Robertson, K. N.

Journal of Dental Research, Vol 70, 874-879, Copyright © 1991 by International & American Associations for Dental Research Online Journals

ARTICLES

Chemical and molecular weight analyses of prosthodontic soft polymers

D. W. Jones, G. C. Hall, E. J. Sutow, M. F. Langman and K. N. Robertson
Department of Applied Oral Science, Faculty of Dentistry, Dalhousie University, Halifax, Nova Scotia, Canada.

A number of studies have been made investigating the properties of dental prosthodontic soft polymer materials. In such materials, which are used as short-term denture soft liners, the polymer component is complexed with one or more plasticizers. This lowers the glass transition temperature, Tg, of the polymer by allowing greater chain mobility and produces a more flexible material. Little information is available relating to the polymer components of such soft-lining materials. The chemical composition and molecular-weight distribution of a polymer help to determine its ability to form a plasticized soft polymer-gel. In the present work, both pyrolysis depolymerization/gas chromatography (GC) and size exclusion chromatography (SEC) have been used to characterize 11 commercial polymer powders. By use of SEC and polymer standards having a narrow molecular-weight range, it has been possible for accurate molecular-weight distributions to be determined for all 11 powders. The peak molecular weights were found to be between 1.79 x 10(5) and 3.28 x 10(5). These values are above the molecular weight at which chain entanglement occurs. The polydispersity ratios (Mw/Mn) were between 2.09 and 4.48. Methacrylate polymers can be readily decomposed thermally to their constituent monomers, which, once recovered, can be analyzed by gas chromatography. The simple pyrolysis apparatus used in the present study was easily assembled and was capable of producing both qualitative and quantitative results. None of the commercial polymers analyzed gave methacrylate decomposition products with pendant chains greater than ethyl (-CH2-CH3). All of the commercial polymers successfully studied by the pyrolysis test method proved to be poly(ethyl [100-79%]/methyl [0-21%] methacrylate) polymers or co-polymers.




HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
IADR Journals Advances in Dental Research ®
Journal of Dental Research ® Critical Reviews (1990-2004)
Copyright © 1991 Institutional Access Guidelines