JDR Woodhead Publishing
HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
QUICK SEARCH:   [advanced]


     

This Article
Right arrow Full Text (PDF)
Services
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Download to citation manager
Citing Articles
Right arrow Citing Articles via Google Scholar
Google Scholar
Right arrow Articles by Asaoka, K.
Right arrow Articles by Tesk, J. A.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Asaoka, K.
Right arrow Articles by Tesk, J. A.

Journal of Dental Research, Vol 69, 463-469, Copyright © 1990 by International & American Associations for Dental Research Online Journals

ARTICLES

Transient and residual stress in a porcelain-metal strip

K. Asaoka and J. A. Tesk
Department of Dental Engineering, School of Dentistry, Tokushima University, Japan.

Porcelain-fused-to-metal (PFM) restorations may develop cracks during processing or in-mouth service if the relative physico-mechanical properties of the porcelain and metal are highly mismatched. Precise conditions when this might occur are not known. Many processing and property variations can affect the stresses developed throughout a porcelain-metal system. To understand this, we conducted a computer simulation of stress developed in a PFM beam. The simulation considers cooling from temperatures higher than the porcelain sagpoint. The following temperature-dependent factors were incorporated: the elastic modulus, shear viscosity (porcelain), and coefficients of thermal expansion. The cooling rate dependencies of the glass transition temperature, (Tg), and the temperature distribution during cooling were also included. The results suggest that transient tensile stress at the porcelain alloy interface may result in cracks in the porcelain during cooling. Occlusal forces may set up stresses to cause cracking at the surface of the porcelain if the compressive residual stress is not high enough. PFM restorations with an alloy of high thermal expansion coefficient require rapid cooling; on the contrary, PFM restorations with the alloys of lower coefficients require slow cooling. A high cooling rate can make up for thermal expansion mismatches between the alloy and the porcelain up to 2 x 10(-6)/degrees C. Finally, the results indicated that curvature was not a sensitive indication of stress for a multimaterial beam when visco-elastic relaxation and high cooling rates are involved. For the case modeled here, curvature varied inversely with a 1/2 to 1/7th power of the stress.




HOME HELP FEEDBACK SUBSCRIPTIONS ARCHIVE SEARCH TABLE OF CONTENTS
IADR Journals Advances in Dental Research ®
Journal of Dental Research ® Critical Reviews (1990-2004)
Copyright © 1990 Institutional Access Guidelines